YTZP 95 Yttria Partially Stabilized Zirconia Grinding Media Ball Size 12mm
Product Details:
| Place of Origin: | Shanxi, China |
| Brand Name: | Zirnano |
| Certification: | ISO9001, IS014001 |
| Model Number: | 0.1mm-50mm |
Payment & Shipping Terms:
| Minimum Order Quantity: | 25kgs |
|---|---|
| Price: | Negotiation |
| Packaging Details: | 25kgs barrels+Pallet |
| Delivery Time: | 5-20 days |
| Supply Ability: | 500mt per year |
|
Detail Information |
|||
| Commodity Name: | Zirconia Milling Beads | Color: | Shiny White |
|---|---|---|---|
| Shape: | Sphere | Bulk Density: | 3.7g/cm3 |
| True Density: | 6.0g/cm3 | Harness: | 1100HV |
| Impact Strength: | 2.0KN | Abrasion Loss: | 0.5ppm/h |
| Chemical Index: | ZrO2 95%Min., Y2O3 4.5%Min. | Port Of Loading: | Tianjin/Qingdao, China |
| Package: | 25kgs Barrels+Pallet | Application: | Grinding Media For Battery, Magnetic Materials, Calcium Carbonate, Titanium Dioxide, Paint, Pigment, Dye, Ink. Etc |
| High Light: | 95 Yttria Partially Stabilized Zirconia,YTZP Yttria Partially Stabilized Zirconia,12mm Yttria Partially Stabilized Zirconia |
||
Product Description
YTZP 95 Yttria stabilized zirconia grinding media ball size 12mm
DESCRIPTION
Yttrium stabilized zirconia balls, also called ceramic grinding beads, 95 zirconia balls, ZY6.0, YTZP etc.
It's produced with micron and sub-nano zirconia as raw materials , mixing about 5% yttrium oxide as a stabilizer.
Density 6.0g/cm3
Features with high grinding efficiency, high strength and toughness without broken beads under high-speed impact;
and ultra-low abrasion.
It is suitable for ultra-fine grinding and dispersion of high viscosity, high hardness, zero pollutant materials.
SPECIFICATION
Manufacturing process: Sintering Method
| Property | Unit | Parameter |
| Index | Wt% | 94.8%ZrO2, 5.2%Y2O3 |
| Bulk Density | Kg/l | 3.7(φ5mm) |
| Density | g/cm3 | 6.00-6.08 |
| Hardness | (HV) | >1200 |
| Modulus of Elasticity | GPa | 200 |
| Thermal Conductivity | W/m.k | 3 |
| Thermal Expansion Coefficient | 10*10-6/℃(20-400) | 9.6 |
| Compressive strength | KN | 2300KN (Φ2.0mm) |
| Crystal size | μm | ≤0.5 |
| SIZES Φ MM for fine grinding | ||||
| 0.1-0.2 | 0.2-0.3 | 0.3-0.4 | 0.4-0.6 | 0.6-0.8 |
| 0.8-1.0 | 1.0-1.2 | 1.2-1.4 | 1.4-1.6 | 1.6-1.8 |
| 1.8-2.0 | 2.0-2.2 | 2.2-2.4 | 2.4-2.6 | 2.6-2.8 |
| 2.8-3.0 |
3.5-4.0mm |
|||
| SIZES Φ MM for rough grinding | ||||
|
Φ5mm, Φ6mm, Φ8mm, Φ10mm, Φ15mm, Φ20mm, Φ25mm, Φ30mm |
||||
FEATURE
1. High strength and toughness without broken beads under high-speed impact;
2. Good sphericity and smooth surface;
3. Ultra-low abrasion
Wear resistance is 30-50 times that of glass beads, 5 times that of zirconium silicate beads, and 6-8 times that of alumina beads.
4. High density and high grinding efficiency
APPLICATION
Mainly used in the grinding and dispersion of electronic ceramics, magnetic materials, alumina powder, quartz, zirconium silicate, titanium dioxide and other high-purity ceramic materials, as well as food, cosmetics, paints, coatings, pigments and inks.
APPLICABLE EQUIPMENT
- YTZP zirconia beads are suitable for
- Vertical sand mills,
- Horizontal sand mills,
- Mixers,
- Ball mills and
- Basket sand mills.